Koriche, N.Brahimi, R.Bellal, B.Trari, M.2022-10-302022-10-30202210231935https://link.springer.com/article/10.1134/S1023193522070072DOI 10.1134/S1023193522070072https://dspace.univ-boumerdes.dz/handle/123456789/10300AgMnO2 nanocrystallites (31 nm) were prepared by sol-gel auto-ignition at 400°C in air. The crednerite characterized by X-ray diffraction (XRD) showed a single phase, crystallizing in a monoclinic unit cell (SG: C2/m). The refinement was made by isotypy with CuMnO2. The oxide is a narrow band-gap semiconductor with an indirect transition at 1.43 eV. The electrical conduction occurs predominantly by small polaron hopping between mixed valences Ag2+/+ in the (a, b) planes with an activation energy of 0.35 eV. The density of holes (NA = 2 × 1015 cm–3) and their mobility (μh = 0.8 × 10–4 m–2 V–1 s–1) indicate a conduction being thermally activated. The oxygen insertion in the layered crystal lattice induces p-type conductivity, a fact confirmed by the electrochemical measurements. The flat band potential (Efb = –0.04 V) indicates a cationic character of both valence and conduction bands deriving mostly from Ag+ 4d-orbital. The electrochemical impedance spectroscopy shows the predominance of the bulk contribution followed by diffusion of O2– species. The energetic band diagram of AgMnO2 established from the photoelectrochemical study, predicts a spontaneous hydrogen formation; a rate evolution of 39 µmol g–1 min–1 and a power conversion of 0.37% were obtained under visible light irradiation (27 mW cm–2)enAuto-ignitionCrednerite AgMnO2HydrogenP-type conductivityVisible lightArticle